Abstract:This research studies the effect of high temperature which is reached to 600 °C onstructural lightweight and normal weight concrete. Lightweight concrete mix designedaccording to ACI committee 211-2-82 with mix proportion 1:1.12 :3.35 by volume .Thewc ratio equal to 0.5 by weight and cement content 550 kgm3. Mix proportions ofnormal weight concrete were 1:2:3 by weight with cement content 400 kgm3 and samewc. The design compressive strength at 28 days of normal weight concrete (NWC) andlightweight concrete (LWC) were 34.7 MPa and 22.62 MPa respectively. Compressivestrength tests were performed on 100 mm cubes exposed to high temperature 100,200,400and 600 °C. The normal weight concrete and light weight concrete test specimens wereexposed to high temperature for 10 minute suddenly at the required degree. Moreover,light weight concrete test specimens tested after graduate exposure to high temperaturereaching to the required degree with and without drying to examine the effect of moisturecontent.The results indicated that the structural lightweight concrete exhibits approximatelysimilar compressive strength loss compared to normal weight concrete up to 600 °C at 28days in graduate exposure .The percentage of reduction on compressive strength was30% in lightweight concrete compared to 28% in normal weight concrete at 600 °C .Insudden exposure to high temperature ,the opposite behavior was noticed .The percentageof reduction on compressive strength was 64.4% in lightweight concrete at 600°C .Drying of lightweight concrete specimens before graduate exposure to high temperaturessignificantly reduce the loss of compressive strength.
AbstractThere is no doubt that the type and properties of cement extremely affect the general properties of produced concrete .Cement is one of the main ingredients of cement past phase in concrete. In present study chemical and physical properties of four types of Portland cement available in Iraqi local market were studied ,these types as follow : two types of ordinary Portland cement Kubaisa (Iraqi cement) and Ismnta (Jordanian cement) and the others of sulfate resisting cement Torab alsabia (Lebanese cement ) and Al-qaim (Iraqi cement).Chemical analysis of the four types of cement were conducted in Baghdad central laboratory in National Center for Constructional Laboratories and Researches (NCCLR) and Al-qaim factory laboratory .The physical tests were conducted in the concrete laboratory of Al_anbar university-college of engineering including standard cement paste ,initial and final setting and compressive strength of cement mortars.The results indicate that the local cement (Kubaisa and Al-qaim) showed better performance than imported cement (Ismnta and Torab alsabia) in most tested chemical and physical properties .Kubaisa cement showed 34.1 % , 35.5 % higher compressive strength compared with Ismnta cement at 3 and 7 day respectively and lower loss on ignition and insoluble residue . The major compounds of Kubaisa cement were nearest to those in typical cement. For sulfate resisting cement , Al-qaim cement showed 13.3 % higher compressive strength at 7 day and lower percentage of C3A (1.95%) . Torab alsabia cement exceed the limits of Iraqi standard I.O.S No.5 1984.
The current research’s purpose is to examine how Ultra-High Performance Fiber Concrete (UHPFC) holds up in terms of strength and durability for strengthening purposes. For this reason, the experimental and the theoretical studies in this research attempted to assess different fresh and hardened properties of a variety of ultra-high performance combinations. Steel fibers were utilized to differentiate all of the program's combinations at percentages of 0.25 %, 0.5 %, 0.75 %, 1%, and 1.25 % by volume. Mini flow slump, compressive and flexural strength, ultrasonic pulse velocity, water absorption, and porosity tests were all used to examine the performance of the strength and durability of the material. The findings of this study's trials showed that steel fibers increased the strength of UHPFC. The steel fiber ratio of 1% gave the maximum compressive strength, whereas 1.25 percent yielded the highest flexural strength. Because the fibers function as a bridge, preventing internal breaking, the tensile test results were improved as the proportion of steel fiber rises. Through the use of the multi-objective optimization approach, the optimal ratio of fibers was chosen at the end of the laboratory work since it has the best durability and strength characteristics. Statistical software (Minitab 2018) was used to find the optimal combination of UHPFC that meets all of the requirements. The theoretical selected optimum ratio of 0.77% of fibers obtained from the optimization was evaluated and validated experimentally. The optimized mix provided 90.28 MPa, 14.6 MPa, and 20.2 MPa for compressive, splitting tensile and flexural tests respectively with better durability performance compared to other mixes prepared in this investigation.
Abstract This research studies the effect of adding steel fiber in two percentage 0.5% and 1% by volume on plain structural lightweight concrete (SLWC) produced by using crushed bricks as coarse lightweight aggregates (LWA) in a lightweight concrete mix designed according to ACI committee 211-2-82 with mix proportion 1:1.12 :3.35 by volume .The wc equal to 0.5 and cement content 550 kgm3. Different tests where performed for fresh and hardened SLWC such slump test ,fresh and hardened unit weight ,compressive strength and two indirect tests of tensile strength (splitting tensile and flexural strength). The results demonstrated that the effect of addition of steel fiber was more pronounced on the tensile strength of SLWC than the compressive strength of such concrete .The maximum increase of compressive ,splitting tensile and flexural strengths at 28-days were 38.8,77.12 and 111.2 % in the SLWC containing 1% fiber. On the other hand the rate of strength gain between 3 and 28 days was constant on compressive strength of plain concrete and that containing steel fiber while this rate was clearly increase on tensile strength especially flexural strength.
This main aim of this study is evaluate wide range of fresh and hardened properties of sustainable self-compacting concrete containing various types of Cement Replacement Materials with optimum contents of Polyethylene Terephthalate PET waste plastic as fibers and fine aggregate replacement. This is to evaluate effect of the two forms of PET and to determine the best CRMs could be used with sustainable SCC. such as limestone, glass powder and fly ash with high replacement rate of 70% by weight of cement were used while fourth one (kaolin) was used with replacement rate of 20%. PET fibers were added to SCC with an aspect ratio of 24.4 and 0.7% volume fraction whereas fine aggregate partially replaced by 4% of waste plastic. Four reference mixtures contained FA, LP, GP and KA only, same four mixtures contained 0.7% PET fibers by volume, and the other same four mixtures contained 4% PET fine aggregate by volume. The obtained results all tested fresh properties, which include slump flow, T500, L-Box and segregation resistance were within the limits of the specification reported in EFNERC guidelines. Further, the forms PET have an adverse effect fresh properties of SCC. As for hardened properties (compressive strength, splitting tensile strength, flexural strength and impact strength). Further, this produced type of SCC showed an range of compressive strength (15.2-31.64 MPa) at 28 days. It can be from the current study the best CRMs to be used in SCC containing PET wastes was FA in terms of most tested properties.